Process For Production Of Commercial Quality Potassium Nitrate From Polyhalite

ABSTRACT

A method for the production of KNO 3  from polyhalite is provided. The method comprises steps of decomposing said polyhalite into syngenite, gypsum, and soluble components, treating the solid decomposition products sequentially with HNO 3  and Ca basic compound, precipitating the CaSO 4  thus formed, and crystallizing the KNO 3  from the solution remaining. The method recovers up to 75% of the potassium present in the raw polyhalite as KNO 3  and substantially all of the remainder as a potassium magnesium sulfate salt.

REFERENCE TO RELATED PUBLICATION

This application claims priority from U.S. provisional application 61/220,232, dated 25 Jun. 2009, which is hereby incorporated by reference in its entirety.

FIELD OF THE INVENTION

This invention concerns improved methods for the production of KNO₃ and potassium and magnesium sulfates from polyhalite.

BACKGROUND OF THE INVENTION

Potassium nitrate, KNO₃, is an industrially important chemical with a variety of uses from fertilizers to explosives. It is primarily obtained either by mining of KNO₃ deposits or by methods that ultimately derive from nitrogen fixation via the Haber process.

Methods for production of KNO₃ from syngenite (K₂Ca(SO₄)₂) are known in the literature. For example, Canadian Pat. No. 1217027 to Worthington et al. and German patent 3525654 to Loblich et al. disclose methods for producing KNO₃ from syngenite via reaction with CaNO₃.4H₂O.

Polyhalite, Ca₂MgK₂(SO₄)₄.2H₂O, is widely distributed and readily available potassium-containing mineral. It has been known for some eight decades (see, for example, Partridge, E. P. Ind Eng. Chem. 1932, 24, 895) that polyhalite can be a useful starting material for production of potash and potassium sulfate. Commercially viable methods that use polyhalite as a starting material for formation of KNO₃ remain as yet unknown, however. A more efficient means for converting raw polyhalite into salts such as potassium nitrate, while increasing the quantity of gypsum relative to that in the raw polyhalite and controlling the relative quantity of KNO₃ and potassium magnesium sulfates produced from the polyhalite, remains a long-felt need.

SUMMARY OF THE INVENTION

The invention herein disclosed is designed to meet this long-felt need. The method herein disclosed recovers at least 45% to 75% of the potassium content of polyhalite, primarily as commercial-quality KNO₃, with the remainder as potassium magnesium sulfate or as a mixture of sulfate salts.

It is therefore an object of the present invention to disclose a continuous method for producing KNO₃ from polyhalite, said method comprising steps of (a) washing polyhalite; (b) heating said washed polyhalite; (c) contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions; (d) separating at least one solid product from said solution; (e) contacting solids obtained from said step of contacting said washed and heated polyhalite with water with a quantity of HNO₃ at least sufficient to produce a slurry; (f) contacting said slurry with an alkaline Ca compound; (g) filtering said slurry; (h) washing gypsum obtained in said steps of contacting said washed and heated polyhalite with water and of treating said slurry with an alkaline Ca compound; (i) concentrating the filtrate obtained in said step of filtering the product of said step of treating said slurry with an alkaline Ca compound; (j) separating at least part of the CaSO₄ contained in said filtrate from the liquid; (k) separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in said filtrate; (1) adding a basic Ca compound to the solution recovered after said step of separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in the filtrate; and (m) separating at least part of the Mg(OH)₂ produced in said step of adding an alkaline Ca compound to the solution recovered after said step of separating KNO₃. It is within the essence of the invention wherein said method is adapted to produce commercial quality KNO₃ from raw polyhalite.

It is a further object of this invention to disclose such a method, wherein between 45% and 75% of the K value of said polyhalite is recovered as KNO₃, and further wherein substantially all of the remaining K value of said polyhalite is recovered in a form chosen from the group consisting of (a) langbeinite, (b) a mixture of Mg and K sulfate salts, and (c) any combination of the above.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of heating said washed polyhalite further comprises an additional step of heating said washed polyhalite to a temperature between about 400° C. and about 500° C.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of heating said washed polyhalite further comprises an additional step of heating said washed polyhalite to a temperature of about 450° C.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions occurs at a temperature between about 20° C. and about 70° C.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions occurs at ambient temperature.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions further comprises an additional step of choosing a polyhalite/water ratio such that substantially all of the Mg²⁺ and less than about 55% of the K⁺ originally present in the raw polyhalite remains in solution.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least one solid product from said solution further comprises an additional step of separating at least one solid chosen from the group consisting of (a) potassium sulfate salts; (b) magnesium sulfate salts; (c) potassium magnesium sulfate mixed salts.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least one solid product from said solution further comprises an additional step of precipitating a solid.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least one solid product from said solution further comprises an additional step of crystallizing said at least one solid product from said solution.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of contacting solids obtained from said step of contacting said washed and heated polyhalite with water with a quantity of HNO₃ at least sufficient to produce a slurry further comprises an additional step of recycling at least part of the solution recovered after said step of separating at least part of the Mg(OH)₂ produced in said step of said alkaline Ca compound to the solution recovered after said step of separating KNO₃.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of contacting said slurry with said alkaline Ca compound further comprises an additional step of contacting said slurry with a quantity of said alkaline Ca compound to reduce the sulfate content by at least 99% while maintaining a pH below 8.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least part of the CaSO₄ contained in said filtrate from the liquid further comprises an additional step of separating more than half of the CaSO₄ contained in said filtrate from the liquid.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least part of the CaSO₄ contained in said filtrate from the liquid further comprises an additional step of separating substantially all of the CaSO₄ contained in said filtrate from the liquid.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least part of the CaSO₄ contained in said filtrate from the liquid further comprises an additional step of separating said CaSO₄ by crystallization.

It is a further object of this invention to disclose such a method, further including an additional step of concentrating said filtrate.

It is a further object of this invention to disclose such a method, further including an additional step of evaporating at least part of the liquid from said filtrate.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of evaporating is effected by a method chosen from the group consisting of (a) multiple effect evaporation; (b) mechanical vapor recompression; (c) solar evaporation.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in said filtrate further comprises an additional step of separating KNO₃ from said solution by crystallization.

It is a further object of this invention to disclose such a method, wherein said step of separating KNO₃ from said solution by crystallization is carried our in a cooling crystallizer.

It is a further object of this invention to disclose such a method as defined in any of the above, further comprising an additional step of purifying the KNO₃ recovered.

It is a further object of this invention to disclose such a method, further comprising an additional step of repulping with a substantially pure KNO₃ solution.

It is a further object of this invention to disclose such a method, further comprising an additional step of recrystallizing said KNO₃.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said step of separating at least part of the Mg(OH)₂ produced in said step of adding Ca(OH)₂ to the solution recovered after said step of separating KNO₃ further comprises an additional step of separating KNO₃ by crystallization.

It is a further object of this invention to disclose such a method as defined in any of the above, further including the additional step of recovering at least, part of the gypsum produced during the process.

It is a further object of this invention to disclose such a method as defined in any of the above, wherein said alkaline Ca compound is chosen from the group consisting of (a) Ca(OH)₂, (b) CaO, (c) CaCO₃, and (d) any combination of the above.

BRIEF DESCRIPTION OF THE FIGURE

FIG. 1 shows a schematic flowchart of a combined process for treatment of polyhalite according to one embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention is described hereinafter with reference to the drawing, in which preferred embodiments are described. For the purposes of explanation, specific details are set forth in order to provide a thorough understanding of the invention. It will be apparent to one skilled in the art that there are other embodiments of the invention that differ in details without affecting the essential nature thereof. Therefore the invention is not limited by that which is illustrated in the figures and described in the specification, but only as indicated in the accompanying claims, with the proper scope determined only by the broadest interpretation of said claims.

Unless specifically indicated to the contrary, chemical formulas are given without regard to the presence or absence of water of hydration, or the stoichiometry of hydration of the salt.

As used herein, the generic term “sulfate salt” includes any salt that contains an anion of the general formula H_(a)S_(b)O_(c) ^(n−), including anions where a=0.

As used herein, the term “crystallizing” includes any technique known in the art for precipitating a solid from a solution.

The method disclosed herein for production of KNO₃ from polyhalite involves the following two sequential chemical reactions, where x represents the fraction of polyhalite converted into syngenite (K₂Ca(SO₄)₂.H₂O); in preferred embodiments of the invention, x is between about 0.45 and about 0.85.

2K₂MgCa₂(SO₄)₄.2H₂O+(4−x)H₂O→xK₂Ca(SO₄)₂.H₂O+(4−x)CaSO₄.2H₂O+2MgSO₄+(1−x)K₂SO₄   (1)

xK₂Ca(SO₄)₂+(4−x)CaSO₄.2H₂O+2xHNO₃+xH₂O+xCa(OH)₂→(4+x)CaSO₄.2H₂O+2xKNO₃   (2)

In summary, in reaction (1), polyhalite is decomposed into syngenite, CaSO₄ (gypsum), and MgSO₄. In reaction (2), the syngenite and gypsum react with nitric acid and calcium hydroxide (introduced separately into the reaction) to yield potassium nitrate.

As discussed in detail below, the reactions are carried out in a series of stages. Reference is now made to FIG. 1, which presents a schematic flowchart of the stages involved in a preferred embodiment 10 of the method disclosed in the present invention for producing KNO₃ from polyhalite.

In the first stage 1010 of the method, polyhalite 101 is washed with sufficient water 102 to remove substantially all of the NaCl contained within the polyhalite. The polyhalite is separated from the supernatant liquid (step 1012), and the supernatant NaC1 solution is then discharged from the system (step 1014).

In the second stage 1020 of the method, the polyhalite undergoes thermal treatment to dry it. In a preferred embodiment, the polyhalite is dried by heating to 450° C. As is well-known in the art, the effectiveness of the drying is demonstrated by the near-total decomposition of the polyhalite in its reaction in the following step of the process. In preferred embodiments, the heating is performed over a period of at least 20 minutes.

Polyhalite decomposition occurs in stage three (1030). In this stage, polyhalite is contacted with water 103. In preferred embodiments of the invention, the reaction takes place at a temperature between about 20° C. and 70° C. In more preferred embodiments of the invention, the reaction mixture is not heated. In a most preferred embodiment of the invention, reaction takes place at ambient temperature. An amount of water sufficient to decompose the polyhalite is added. The polyhalite decomposes to yield as insoluble products syngenite and gypsum (CaSO₄.2H₂O). The polyhalite:water ratio and the temperature are chosen such that substantially all of the Mg²⁺ and less than about 55% of the K⁺ contained in the polyhalite is dissolved; in preferred embodiments, the polyhalite:water ratio (w/w) ranges from about 2:5 to 2:3. This reaction, and means for optimizing the polyhalite:water ratio, are well-known in the art. The syngenite is then separated from the supernatant liquid and washed (step 1032).

In stage 4 (1040), the solution containing Mg²⁺, K⁺, SO₄ ²⁻, and traces of Ca²⁺ obtained in the previous stage is concentrated sufficiently to precipitate at least part of the dissolved material to provide solid product 204. In preferred embodiments, the concentration is performed by crystallization. In some embodiments of the invention, MgSO₄ solution recycled from stage 8 described below is added to the solution. In preferred embodiments, the solution is concentrated sufficiently to produce solid product 204 K_(x)Mg_(y)(SO₄)_((x/2+y)) as a mixture of langbeinite (K₂Mg₂(SO₄)₃) and hydrated MgSO₄. In some embodiments of the invention, the salts are crystallized separately, while in other embodiments, they are crystallized as a mixture.

In stage 5a of the method (1050), the solids precipitated in stage 3 are treated with HNO₃ (105) in order to obtain a solution containing K⁺, Ca²⁺, and NO₃ ⁻, along with small quantities of Mg²⁺ and SO₄ ²⁻, as well as undissolved solids comprising primarily gypsum. In stage 5b (1052) the slurry obtained in stage 5a is further treated with Ca(OH)₂ (106) to precipitate the sulfate as gypsum (205) and to bring the solution substantially to neutral pH. The gypsum precipitated in stages 5a and 5b (step 1054) is washed with water (in preferred embodiments, by counter-current washing on a filter or by continuous washing in equipment) in order to reduce the nitrate content.

In stage 6 (1060), the supernatant liquid obtained in stage 5 is concentrated (in preferred embodiments, by evaporation by methods well-known in the art, e.g. in a multiple effect evaporator, by mechanical vapor recompression, or by solar evaporation). In some embodiments of the invention, the CaSO₄ precipitated (206) is separated from the solution (1062) at the exit from the evaporator (in preferred embodiments, by a polishing filter). In embodiments in which solar evaporation is performed, the CaSO₄ is left on the bottom of the pond.

In stage 7 (1070), KNO₃ (208) is separated from the solution. In preferred embodiments of the invention, the separation is accomplished by crystallization. In most preferred embodiments, the crystallization is carried out in a cooling crystallizer of any appropriate type known in the art, for example, a cooling disc crystallizer. In some embodiments of the invention, the KNO₃ produced in stage 7 is further purified by repulping with a pure KNO₃ solution or by further recrystallization.

In stage 8 of the method (1080), a second stream comprising an alkaline Ca compound is added to the solution recovered from the crystallizer in order to precipitate the major part of the Mg²⁺ remaining in the solution. The solid Mg(OH)₂ (207) thus precipitated can be used as obtained, or reacted with H₂SO₄ and the resulting solution added to the solution concentrated in stage 4, as described above. In preferred embodiments, the solution remaining after the crystallization step in stage 8 (107) is recycled into the solution used in stage 3, wherein at least a portion of the Ca(NO₃)₂ in the solution reacts with at least a portion of the sulfate to precipitate gypsum.

EXAMPLES Example 1

Polyhalite was washed with water to remove NaCl and then dried at 450° C. 200 g of washed and dried polyhalite were mixed with 500 g of water at 50° C. After two hours, the slurry was filtered. The solution comprised 1.7% K⁺, 1.5% Mg²⁺, and 8.1% SO₄ ⁼ (w/w).

The solid was examined by XRD; the phases identified were gypsum and syngenite. The solid comprised 16.3% Ca²⁺, 11.3% K⁺, 0.75% Mg²⁺ and 55% SO₄ ⁼. More than 70% of the potassium of the polyhalite remained in the solid phase, while about 85% of the Mg was dissolved.

Example 2

Polyhalite was washed with water to remove NaCl and then dried at 450° C. 200 g of washed and dried polyhalite were mixed with 400 g of water at 50° C. After two hours, the slurry was filtered. The solution comprised 2.2% K⁺, 1.4% Mg²⁺, and 8.% SO₄ ⁼.

The solid comprised 19% Ca²⁺, 6.8% K⁺, 0.8% Mg²⁺ and 57% SO₄ ⁼. About 45% of the potassium content of the polyhalite remained in the solid phase, while about 85% of the Mg was dissolved.

Reaction of 100 g of the wet solids with 23 g of HNO₃ (60%) in presence of 900 g of water yielded a solution comprising 3.8% K⁺ and 0.5% Mg²⁺, while the solid residue contained less than 0.1% of both Mg²⁺ and K⁺. 

1-26. (canceled)
 27. A continuous method for producing KNO₃ from polyhalite, said method comprising steps of: washing polyhalite; heating said washed polyhalite; contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions; separating at least one solid product from said solution; contacting solids obtained from said step of contacting said washed and heated polyhalite with water with a quantity of HNO₃ at least sufficient to produce a slurry; contacting said slurry with an alkaline Ca compound; filtering said slurry; washing gypsum obtained in said steps of contacting said washed and heated polyhalite with water and of treating said slurry with an alkaline Ca compound; concentrating the filtrate obtained in said step of filtering the product of said step of treating said slurry with an alkaline Ca compound; separating at least part of the CaSO₄ contained in said filtrate from the liquid; separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in said filtrate; adding a basic Ca compound to the solution recovered after said step of separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in the filtrate; and, separating at least part of the Mg(OH)₂ produced in said step of adding an alkaline Ca compound to the solution recovered after said step of separating KNO₃; wherein said method is adapted to produce commercial quality KNO₃ from raw polyhalite.
 28. The method according to claim 27, wherein between 45% and 75% of the K value of said polyhalite is recovered as KNO₃, and further wherein substantially all of the remaining K value of said polyhalite is recovered in a form chosen from the group consisting of (a) langbeinite, (b) a mixture of Mg and K sulfate salts, and (c) any combination of the above.
 29. The method according to claim 27, wherein said step of heating said washed polyhalite further comprises an additional step of heating said washed polyhalite to a temperature between about 400° C. and about 500° C.
 30. The method according to claim 27, wherein said step of heating said washed polyhalite further comprises an additional step of heating said washed polyhalite to a temperature of about 450° C.
 31. The method according to claim 27, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions occurs at a temperature between about 20° C. and 70° C.
 32. The method according to claim 27, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions occurs at ambient temperature.
 33. The method according to claim 27, wherein said step of contacting said washed and heated polyhalite with sufficient water to produce decomposition products comprising K₂Ca(SO₄)₂, gypsum, and a solution comprising K⁺, Mg²⁺, and SO₄ ²⁻ ions further comprises an additional step of choosing a polyhalite/water ratio such that substantially all of the Mg²⁺ and less than about 55% of the K⁺ originally present in the raw polyhalite remains in solution.
 34. The method according to claim 27, wherein said step of separating at least one solid product from said solution further comprises an additional step of separating at least one solid chosen from the group consisting of (a) potassium sulfate salts; (b) magnesium sulfate salts; (c) potassium magnesium sulfate mixed salts.
 35. The method according to claim 27, wherein said step of separating at least one solid product from said solution further comprises an additional step chosen from the group consisting of (a) precipitating a solid and (b) crystallizing at least one solid product from said solution.
 36. The method according to claim 27, wherein said step of contacting solids obtained from said step of contacting said washed and heated polyhalite with water with a quantity of HNO₃ at least sufficient to produce a slurry further comprises an additional step of recycling at least part of the solution recovered after said step of separating at least part of the Mg(OH)₂ produced in said step of said alkaline Ca compound to the solution recovered after said step of separating KNO₃.
 37. The method according to claim 27, wherein said step of contacting said slurry with said alkaline Ca compound further comprises an additional step of contacting said slurry with a quantity of said alkaline Ca compound to reduce the sulfate content of the solution by at least 75% while maintaining a pH below
 8. 38. The method according to claim 27, wherein said step of separating at least part of the CaSO₄ contained in said filtrate from the liquid further comprises an additional step of separating substantially all of the CaSO₄ contained in said filtrate from the liquid.
 39. The method according to claim 27, wherein said step of separating at least part of the CaSO₄ contained in said filtrate from the liquid further comprises an additional step of separating said CaSO₄ by crystallization.
 40. The method according to claim 39, further including an additional step of concentrating said filtrate.
 41. The method according to claim 40, further including an additional step of evaporating at least part of the liquid from said filtrate.
 42. The method according to claim 27, wherein said step of separating KNO₃ from the solution recovered after said step of separating at least part of the CaSO₄ contained in said filtrate further comprises an additional step of separating KNO₃ from said solution by crystallization.
 43. The method according to claim 27, further comprising an additional step of purifying the KNO₃ recovered.
 44. The method according to claim 27, wherein said step of separating at least part of the Mg(OH)₂ produced in said step of adding Ca(OH)₂ to the solution recovered after said step of separating KNO₃ further comprises an additional step of separating KNO₃ by crystallization.
 45. The method according to claim 27, further including the additional step of recovering at least part of the gypsum produced during the process.
 46. The method according to claim 27, wherein said alkaline Ca compound is chosen from the group consisting of (a) Ca(OH)₂, (b) CaO, (c) CaCO₃, and (d) any combination of the above. 